Investigation of dislocation structure of low carbon steel during static loading

Dislocation structure changes of low carbon steel in both surface and internal metal layers at static loading were investigated in this article. The analysis carried out by us using layer-by-layer electron microscopy has shown, that at all stages of deformation the character of an arrangement and density of dislocations essentially varies at moving away from the surface in to depth of the emtal. At small degrees of deformation plastic flow of the emtal is limited by surface layer. At higher degrees of deformation the internal layers of the metal are involved in to plastic flow. Especially big difference between dislocation structures of surface and internal layers of a meterial is observed in the field of the upper yield limit.

Straipsnyje tiriama, kaip keičiasi dislokacinės struktūros mažaanglio plieno paviršiniame ir vidiniuose sluoksniuose statinio apkrovimo metu. Peršviečiamosios elektroninės mikroskopijos tyrimai parodė, kad visose deformacijos stadijose dislokacijų išsidėstymas ir jų tankis smarkiai skiriasi einant nuo metalo paviršiaus į vidinius sluoksnius. Esant mažiems deformacijos laipsniams, plastiškai deformuojasi tik paviršinis metalo sluoksnis. Didinant deformacijos laipsnį, plastinė deformacija pastebima ir vidiniuose sluoksniuose. Ypač didelis paviršinio ir vidinių metalo sluoksnių dislokacinės struktūros skirtumas pastebimas takumo stadijoje.